seria: Additive manufacturing technology of electroactive three-dimensional structures from diamond reinforced polylactide composites liczba: 32
rozwiń zwiń-
The electrochemical studies for chitosan hydrogel membranes on glassy carbon substrates
Dane BadawczeThis dataset contains various electrochemical studies carried out to investigate the preconcentration of [Fe(CN)6]3- ions by chitosan hydrogel membranes coating the glassy carbon electrodes. The glassy carbon electrode (GCE, 3.0 mm diameter) was first polished with Al2O3 powder (0.3 mm) using a polishing kit from Buehler, rinsed with deionized...
-
The influence of chitosan hydrogel cross-linking by agarose on coating physico-chemical properties
Dane BadawczeThis dataset contains various physicochemical analyses showing the effect of different concentration of chitosan and the cross-linking agent agarose. Each sample is labeled by C and A representing chitosan and agarose concentrations, respectively, while the exact amounts are depicted in the attached table. Fourier-transform infrared (FT-IR) spectroscopy...
-
The influence of chitosan hydrogel coating on different redox probes kinetics
Dane BadawczeThis dataset contains cyclic voltammetry studies of three redox probes: 1 mM K3[Fe(CN)6], [K4Fe(CN)6], C12H14FeO2, and [Ru(NH3)6]Cl2 dissolved in 0.1 M KCl or PBS as the primary electrolyte. The studies are made for glassy carbon electrode (GC) and glassy carbon electrode covered with thin chitosan hydrogel membrane (C2A2). Cyclic voltammograms were...
-
Raman studies of 3D printed CB-PLA samples after microwave treatment
Dane BadawczeThis dataset contains Raman spectroscopy analyses of microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Dane BadawczeThis dataset contains the electrochemical studies on microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Dane BadawczeThis dataset contains the SEM micrographs of carbon-black doped polylactic acid 3D printed electrodes, after microwave treatment to activate the electrode surfaces. FEI Quanta 250 FEG SEM was used for these analyses. Samples were treated with CEM reactor or microwave oven.
-
Mechanical durability and electroanalytical performance of 3D-printed multi-material sensors
Dane BadawczeThe data set consists tensile strength, electric resistance, electrochemical characteristics and physicochemical studies of multi-material 3D printed systems, including their sensing performance during detection of antibiotics in an industrial sewage. Additionally, contact angle measurements and SEM micrographs of the electrode surfaces were included.
-
Broadband dielectric spectroscopy studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains broadband dielectric spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Thermal analyses of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains thermal analyses (TGA, DTG, DSC) studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Topography studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains topography studies with scanning electron microscope of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material...
-
Electrochemical analyses of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains cyclic voltammetry studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Electrochemical studies for screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains electrochemical examination of SPCE paste and SPCE containing boron-doped diamond BDD foils. The studies include kinetics analyses with cyclic voltammetry and electrochemical impedance spectroscopy with different redox probes: hexacyanoferrate(III) and Hexaammineruthenium(III) and potentiostatic open circuit potential at different...
-
Performance of Haemophilus influenzae impedimetric biosensors based on screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains electrochemical impedance spectroscopy studies of SPCE electrodes containing boron-doped diamond BDD foils and functionalized towards detection of Protein D and Haemophilus influenzae.
-
Physicochemical studies (Raman, XRD) of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains physico-chemical examination of a new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include Raman spectroscopy and X-ray diffraction...
-
Physicochemical studies (BET) of nanoparticles used for 3D printable conductive composites
Dane BadawczeThis dataset contains physico-chemical examination of fillers used to fabricate new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Geometric surface area of the nanoparticles was studied by Brunauer–Emmett–Teller (BET) adsorption/desorption isotherms. Investigated samples: CB Ensaco 250G, detonation...
-
Electrochemical studies of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains electrochemical investigation on electrodes 3D printed using a new composite composed of poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The presented results contain:1. electrochemical characterisation...
-
Rheology studies of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains rheology measurements carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was performed by melt mass-flow rates (MFR)....
-
New 3D printable filaments with nanodiamonds, physicochemical additives characteristics and electrochemical activity
Dane BadawczeThis dataset contains the physicochemical analyses (XRD, Raman spectroscopy, BET analyses) and electrochemical analyses (CV, EIS) for a new 3D-printable composite has been developed dedicated to electroanalytical applications. Two types of diamondised nanocarbons - detonation nanodiamonds (DNDs) and boron-doped carbon nanowalls (BCNWs) - were added...
-
Raman spectroscopy analysis of poly(lactic acid)-carbon black composite treated by femtosecond laser
Dane BadawczeThe dataset contains the Raman spectroscopy measurements of commercially available carbon black-filled poly(lactic acid) 3D printed electrodes after femtosecond laser ablation. These results were utilized in the manuscript published in Electrochimica Acta: 10.1016/j.electacta.2022.140288
-
Partial PLA composite surface activation by femtosecond laser ablation
Dane BadawczeThe dataset contains the studies on electrochemical activity of PLA composite (commercially available CB-PLA Protopasta), which was 3D printed in a form of 1x1cm electrodes. The electrodes were submitted to femtosecond laser ablation, etching a certain % of the electrochemically-exposed electrode size. The % value is in the name of each file. The goal...
-
Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser
Dane BadawczeThe dataset contains the scanning electrochemical micrographs of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Images revealing the effect of local femtosecond laser ablation of conductive poly(lactic acid) 3D printed electrodes
Dane BadawczeThe dataset reveals the images of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Partial PLA composite surface activation by femtosecond laser ablation
Dane BadawczeThe dataset contains the studies on electrochemical activity of PLA composite (commercially available CB-PLA Protopasta), which was 3D printed in a form of 1x1cm electrodes. The electrodes were submitted to femtosecond laser ablation operating with different parameters. These were: gas atmosphere (He or air, data in different subfolders), the percentage...
-
The topography of carbon black-polylactide composite 3D printed electrodes after femtosecond laser ablation
Dane BadawczeThis dataset contains a series of scanning electron microscopy images revealing the topography of 3D printed carbon black-polylactide composite electrodes after laser ablation with a femtosecond laser. Different laser powers were investigated, namely: 10%, 25%, 50%, 75% and 100%. The CB-PLA electrodes were 3D printed using an Ender printer. Femtosecond laser NKT Photonics, Origami XP parameters: power at 100%...
-
Caffeine detection using CB-PLA electrode after Nd:YAG laser ablation in He atmosphere
Dane BadawczeThe dataset contains electrochemical studies in form of cyclic voltammetry (CV) and differential pulse voltammetry (DPV) of laser-activated 3D printed CB-PLA electrodes. The ablation of the 3D-printed CB-PLA electrodes was carried out using a pulsed LaserBlast 500 Nd:YAG laser (Quantel, France) operating at 1064 nm and a 6 ns pulse duration.
-
The XPS studies of the CB-PLA electrodes after different surface treatments (chemical, electrochemical, enzymatic)
Dane BadawczeThe dataset contains the Xray Photoelectron Spectroscopy results of the studies performed under different conditions of surface activation of the CB-PLA 3D printed electrodes. The activation was performed by hydrolysis in different solvents (DMF, 1M HCl, 1M NaOH), electrolysis in 1M NaOH, enzymatic treatment in polymerase or simultaneous electrolysis...
-
Surface activation by cyclic polarization in 1M HCl and its effects on the electrochemical response of CB-PLA 3D printed electrodes
Dane BadawczeThe dataset contains the electrochemical studies performed for surface activation of the CB-PLA 3D printed electrodes by electrolysis in 1M HCl solution. The studies were performed after treatment at different polarization ranges, as labeled in subfolder names. For each electrode the consecutive studies describe different samples, as labeled in subfolders:...
-
The cyclic voltammetry studies of CB-PLA electrode after surface activation by electrolysis in 1M NaOH
Dane BadawczeThe dataset contains the electrochemical studies performed for surface activation of the CB-PLA 3D printed electrodes by electrolysis in 1M NaOH solution. The studies were performed after treatment at an anodic overpotential of 1V, found to be optimal for surface activation. The measurements were carried out with cyclic voltammetry (CV) under different...
-
The electrochemical studies of CB-PLA electrode after surface activation by proteinase K digestion
Dane BadawczeThe dataset contains the electrochemical studies performed to evaluate surface activation of the CB-PLA 3D printed electrodes by enzymatic hydrolysis in a solution containing proteinase K (72h digestion period). Different enzyme concentrations were evaluated: 0.2, 0.4, 0.6 and 0.8 mg/ml. The studies were performed before surface activation, during and...
-
The electrochemical studies of CB-PLA surface activation by electrolysis in 1M NaOH
Dane BadawczeThe dataset contains the electrochemical studies performed under different conditions of surface activation of the CB-PLA 3D printed electrodes. The activation was performed by electrolysis in 1M NaOH solution under cycling polarization with different anodic or cathodic overpotentials (data in different subfolders). The file names contain the exact...
-
The electrochemical studies of CB-PLA electrode after surface activation by proteinase K digestion with different times and concentrations
Dane BadawczeThe dataset contains the electrochemical studies performed to evaluate surface activation of the CB-PLA 3D printed electrodes by enzymatic hydrolysis in a solution containing proteinase K. DIfferent proteinase K concentrations and digestion times were evaluated, as described in subfolder names. The studies were performed before surface activation, during...
-
The scanning spreading resistance microscopy (SSRM) studies of heavy boron-doped diamond oxidation under high-temperature
Dane BadawczeThe dataset contains the results of scanning spreading resistance microscopy (SSRM) of heavy boron-doped diamond (BDD) electrodes subjected to high-temperature oxidation in a furnace at 600 Celsius. The micrographs reveal the local change of electric properties at certainly crystallographic orientations of BDD grains and at the grain boundaries due...
-
The scanning electron microscopy (SEM) studies of heavy boron-doped diamond oxidation under high-temperature
Dane BadawczeThe dataset contains the results of scanning electron microscopy (SEM) images of heavy boron-doped diamond (BDD) electrodes subjected to high-temperature oxidation in a furnace at 600 Celsius. The micrographs reveal the material decomposition of BDD grains due to high temperature.
-
Evaluation of the content of zinc compounds in polyethylene films using scanning electron microscopy
Dane BadawczeThe dataset contains the results of in the form of micrographs made using a scanning electron microscope (SEM) S–3400N (Hitachi, Hyogo, Japan) using backscattered electron (BSE) detector. SEM was equipped with tungsten filament. The accelerating voltage was 25 kV. Utilization of BSE detector allowed to increase the contrast of local areas varying in...
-
Dynamic impedance data for various carboxylic acids corrosion inhibition of aluminium in alkaline media (pH=11)
Dane BadawczeThis dataset contains the results of Dynamic Electrochemical Impedance Spectroscopy (DEIS) carried out in galvanostatic mode under iDC=0, carried out in order to define the corrosion inhibition effect of various studied carboxylic acids: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, carballylic acid, and serine. The experiment...
-
X-ray Photoelectron Spectroscopy studies of various carboxylic acids adsorption on aluminium alloys in alkaline media
Dane BadawczeThis dataset contains the results of high-resolution XPS studies obtained during evaluation of high corrosion inhibition efficiency of various carboxylic acids towards aluminium alloy 5754 in bicarbonate buffer pH=11.