The XAS spectra of O-K edges, M-L edges and Ce-M edges in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of XAS spectra of O-K edges, M-L edges of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) synthesised by reverse microemulsion method. XAS spectra were collected at PIRX beamline in SOLARIS National Synchrotron Radiation Centre. Measurements were perfomed under ultra high vacuum in total electron yield (TEY) mode.
-
The 3d Ce XPS spectra of Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 3d Ce XPS of Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons were excited by an...
-
The 2p XPS spectra of transition metals in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 2p XPS spectra of transition metals in Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons...
-
The TPR reduction profile of Ce0.9M0.1O2
Dane BadawczeThe dataset includes the TPR reduction profiles of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared by the reverse microemulsion method. After the synthesis powders were dried, then calcined at 500 degrees for 2 h. The measurements were carried out in H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min.
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
The XRD diffraction patterns of Ce0.9M0.1O2 prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution using tetramethylammonium hydroxide (TMAOH). After the precipitation, the sediment was centrifuged and rinsed with alcohol several times. Precursors powder...