Complex modulus of Cement Bitumen Treated Material Mixture C3E4 cores obtained from the field section (28-365 days of curing at the field and later in laboratory at 20C)

Opis

Dataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Specimen were obtained from the field at 28, 180, 270 and 365 days after compaction. Mixture contains 70% of RAP material. Specimen size: f=100 mm, h=150mm.

Data was obtained on the Simple Performance Tester (IPC global) for 1 temperatures (+20°C) and varied curing times (28, 42, 90, 180, 270 and 365 days - see description in the dataset). Gauge length was 70 mm.

Test load was selected as haversine compression with varied target strain range – from 10-20µstrain up to 200-210µstrain.

Plik z danymi badawczymi

Linearity check - Complex Modulus (SPT) - Cores obtained from the field (Argentum).xlsx

54.3 kB, S3 ETag f34c9a4e80081594d400ff3685fd8344-1, pobrań: 47

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC

Użycie niekomercyjne

Informacje szczegółowe

Rok publikacji:

2024

Data zatwierdzenia:

2024-01-19

Język danych badawczych:

angielski

Dyscypliny:

inżynieria lądowa, geodezja i transport (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/p6ph-mx41

Seria:

Argentum I, IDUB

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja The dependence of linear viscoelasticity limits of cold-recycled mixtures on time of curing and compaction method

Cytuj jako

Autorzy

wyświetlono 97 razy

Wyszukiwarka