Complex modulus of Cement Bitumen Treated Material Mixture C3E4 laboratory mixed/laboratory compacted (7-365 days of curing at 20C)

Opis

Dataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in laboratory conditions on the basis of materials obtained from the contractor and later compacted in laboratory. Mixture contains 70% of RAP material. Specimen size: f=100 mm, h=150mm.

Data was obtained on the Simple Performance Tester (IPC global) for 1 temperatures (+20°C) and 7 curing times (7, 14, 28, 42, 90, 180 and 365 days). Gauge length was 70 mm.

Test load was selected as haversine compression with varied target strain range – from 10-20µstrain up to 200-210µstrain.

Plik z danymi badawczymi

Linearity check - Complex Modulus (SPT) - Laboratory compacted specimen - laboratory mixed (Argentum).xlsx

59.0 kB, S3 ETag 51bf9dbe049f87a3bf8d46e7a65b0f31-1, pobrań: 5

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC

Użycie niekomercyjne

Informacje szczegółowe

Rok publikacji:

2024

Data zatwierdzenia:

2024-01-19

Język danych badawczych:

angielski

Dyscypliny:

inżynieria lądowa, geodezja i transport (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/qkgb-kz66

Seria:

Argentum I, IDUB

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja The dependence of linear viscoelasticity limits of cold-recycled mixtures on time of curing and compaction method

Cytuj jako

Autorzy

wyświetlono 28 razy

Wyszukiwarka