Imaging of the effects of pitting corrosion with the use of AFM

Opis

Pitting corrosion is a local attack on a metal surface, limited to a point or small area, which appears as a hole. Pitting corrosion is one of the most harmful forms of corrosion due to the fact that it is associated with small, difficult to detect damage, that can even lead to perforation of the structure. A single pit may range in size from micrometers to millimeters, which may make it difficult to identify it quickly. This type of corrosion usually occurs in alloys that are protected by a permanent oxide layer, such as stainless steels, nickel alloys, aluminium alloys, in environments containing aggressive compounds such as chlorides or thiosulphates. The measurements included in the set were made on the surface of AISI304 high-alloy steel, previously subjected to anodic electrochemical polarization in a 3% brine solution, in order to induce a local attack process. Measurements were made on the dried surface of the sample using the semi-contact technique with the use of the NSG30 probe. The collection contains 14 images.

[1] P. Guo, E.C. La Plante, B. Wang, X. Chen, M. Balonis, M. Bauchy, G. Sant, Direct observation of pitting corrosion evolutions on carbon steel surfaces at the nano-to-micro- scales, Sci. Rep. 8 (2018) 7990. doi:10.1038/s41598-018-26340-5.

Plik z danymi badawczymi

set20.mdt

1.8 MB, S3 ETag 0fd19203a2e5cea8814066843b9a6a38-1, pobrań: 56

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC

Użycie niekomercyjne
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-05-28

Język danych badawczych:

angielski

Dyscypliny:

nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)

DOI:

10.34808/fpwr-b337

Seria:

Scanning Probe Microscopies data

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 152 razy

Wyszukiwarka