Opis
Ceramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed by X-Ray photoemission spectroscopy (XPS). XPS analysis were performed at room temperature under a pressure below 1.1 × 10−9 mBar. The photoelectrons were excited by an Mg-Kα X-Ray anode operated at 15 keV and 300 W. Omicron Argus hemispherical electron analyser with a round aperture of 4 mm was used for the analysis of emitted photoelectrons. Measurements were carried out in a constant analyser energy (CAE) mode with pass energy equal 50 eV. To remove contaminations and oxides, the surface was etched before the measurement. Argon ion gun with energy up to 5 keV was used for 5 min. etching. In this dataset La3d high resolution spectra for each samples are presented.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-07-19
- Data wytworzenia:
- 2019
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/n7yd-3w16 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Cytuj jako
Autorzy
wyświetlono 32 razy