Linear impedance of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region

Opis

The linear electrical properties of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.

The composition of 2Si3N4–98(40Na2O-20CaO-40P2O5) (in mol%) was prepared by the conventional melt quenching technique. Appropriate amounts of reagents: NaH2PO4 (≥99.5% SIGMA ALDRICH), Na2CO3 (99.9+% ChemPur GmbH) and CaCO3 (99.9+% ChemPur GmbH), Si3N4 (99.9+% ChemPur GmbH) were thoroughly mixed. Batches were melted in porcelain crucibles at temperatures of 850–950 degC for 30–60 min, in air atmosphere. Melt was poured on a brass plate. The exact composition of samples was checked with the use of SEM-EDS and wa sfound to be Na17.3Ca4.6P16.6Si1.3O58N2.1 in at%.

For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the temperature range from 153 K to 423 K, in the frequency range from 10mHz to 1 MHz and with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer.

Plik z danymi badawczymi

128.zip

200.5 kB, S3 ETag b7e9e17c6e8de85eb60bb9df54c143a4-1, pobrań: 57

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2018

Data zatwierdzenia:

2021-07-19

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/vj5t-t870

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 132 razy

Wyszukiwarka