Nonlinear impedance of vanadate glass-ceramics containing BaTiO3

Opis

The nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass plate and pressed by another plate to obtain flat circular pellets of 1–2 mm thickness and 10–20 mm in diameter. A subset of as-quenched samples was heat treated in air at the temperature of 633 K (close to the crystallization temperature) for 6 h and cooled with the furnace. For the electrical measurements gold electrodes were evaporated at the preheated samples. Nonlinear Impedance measurements were carried out in the frequency range from 1 mHz to 1 MHz and the temperature range from 153 K to 423 K, with the ac voltage of 1 Vrms with Concept 40 broadband dielectric spectrometer. The higher harmonic components (harmonic 0, harmonic1 and harmonic2) were measured up to frequency of 1000 Hz. Here the impedance for harmonic components was defined as the ratio of the voltage base wave to the n-th harmonic current component: Zn∗= U0∗/In∗, where Zn⁎ including the base wave generally depend on the sample voltage U1⁎ base wave amplitude. From Zn⁎ allother independent variables are calculated. The dependence of current density on the cosinusoidal electric field E(t)= E0cos(ωt) leads to the following expression:
j´ = σ´0hE0 cos (ωt) + σ´1hE0 cos (2ωt) + σ´2hE0 cos (3ωt) + …
Where σ´0h denotes base conductivity, while σ´1h, σ´2h etc. are higher harmonics conductivity. The admittivity for harmonic components with n ≥1, is calculated from relation σ⁎n = i2πfε0ε⁎n.

Plik z danymi badawczymi

set21.zip

188.0 kB, S3 ETag 976936b9efa3af5b8fc7aaf83835547f-1, pobrań: 54

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-05-24

Data wytworzenia:

2013

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/fa92-c376

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Nanostructure and dielectric behavior of vanadate glasses containing BaTiO3

Cytuj jako

Autorzy

wyświetlono 122 razy

Wyszukiwarka