Plasmon resonance in a TiO2-Au NPs structures - Open Research Data - MOST Wiedzy

Twoje konto

zaloguj

Wyszukiwarka

Plasmon resonance in a TiO2-Au NPs structures

Opis

Investigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering system (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements, was used. Films were deposited from a high purity (99.99%) gold target in pure argon (99.999%) plasma. For film deposition with a rate of ca. 0.1nm/s, ca. 10W of incident power was applied. Annealing of gold thin film, for 15 min at 550 °C in air atmosphere, resulted in forming spherical isolated islands. 

TiO2 thin film, with thickness of 200 nm, was prepared by radio frequency (RF) magnetron sputtering process, using Omicron NanoScience, four targets sputter system. Ti target was sputtered in an argon-oxygen atmosphere (Ar:O2 flow ratio: 5sccm:30sccm, both gasses with purity of 99.999%). Used of RF power of 60W resulted in deposition with a ratio ca. 0.05 nm/s. Substrates with plasmonic nanostructures were heated to 200 ⁰C during TiO2 film deposition process.

Optical properties of manufactured structures were investigated using Evolution 220 UV-Visible Spectrophotometer in a range of 200 nm – 1000 nm. Measured optical properties of structures with various thickness of initial Au layer (1.5, 2.8 and 4.0 nm) and various profiles of heating, during manufacturing.

Plik z danymi badawczymi

AuTiO2-porównanie-z-TiO2Au.opj
274.8 kB, S3 ETag 21946ca48118aa29df07e9ab86280110-1, pobrań: 43
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:
origin

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-07-14
Data wytworzenia:
2019
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/q0pe-8619 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 102 razy