The electrical conductivity of pristine, La-, and Nb-doped SFM measured in air and hydrogen atmospheres

Opis

This dataset consists of an Excel sheet with the result of DC4W method of electrical measurements. The measurements were conducted on pristine strontium ferrite molubdate as well as ones doped with La and Nb. Additionally two samples co-doped with La and Ni/Co were analyzed. Pellets were prepared by high temperature sintering at 1400 deg. C, then cut into rectangles. Platinum electrodes were mounted and samples were put into the measurement cell. Firstly sample were heated up to 900 deg. C in air, then datapoints were collected during cooling. Each temperature was hold for several hours to allow relaxation. Then the gas was switched to inert gas, to rinse the cell before enabling the hydrogen flow. Same procedure was repeated for hydrogen atmosphere.

Plik z danymi badawczymi

Electrical_conductivity_012023_SFM_LSFM(10Co, 10Ni)_SFMNb.xlsx

85.8 kB, S3 ETag 7e261446728254652038788bfb195d7e-1, pobrań: 6

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Embargo na plik:: 2025-06-15

Informacje szczegółowe

Rok publikacji:

2024

Data zatwierdzenia:

2024-01-15

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/f06g-w664

Finansowanie:

Wpływ nanocząstek wydzielonych na podwójnym perowskicie na efektywność ogniw paliwowych zasilanych biogazem

Seria:

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 102 razy

Wyszukiwarka