The luminescence study of Sr2TiO4:Sm3+ coumpounds.

Opis

A luminescent material based on the strontium orthotitanate (Sr₂TiO₄) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence properties as well as to determine the position of the energetic states of Sm³⁺ in relation to the valence and conduction bands of Sr₂TiO₄. The XRD result shows that the product of the synthesis is pure Sr₂TiO₄. From the PL spectra, it can be seen that the phosphor can be effectively excited at 409 and 342 nm to emit significantly different emission spectra. The luminescence obtained under 409 nm excitation is typical of Sm³⁺ in Sr₂TiO₄ and attributed to the nonsymmetrical luminescent center (A-center). In contrast, the luminescence obtained under excitation at 342 nm originates from the symmetrical center (B-center) and has not been reported in the literature so far. The presence of the two emission centers related to Sm³⁺ ions in the Sr₂TiO₄ matrix characterized by only one crystallographic site of Sr²⁺ was explained by considering the different ways of charge compensation: Sm³⁺ in the A-center via strontium vacancy (V′′_sr), and Sm³⁺ in the B-center via Ti³⁺ (Ti′_Ti).

In that dataset, the scientific article, raw data of X-ray diffraction, photoconductivity, excitation and emission spectra, and temperature-dependent photoluminescence and decay profiles are provided.

Plik z danymi badawczymi

Energetic structure of Sm3+ luminescence centers.rar

4.8 MB, S3 ETag 6ab5304688a3fae9202427c38cfc57d5-1, pobrań: 69

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: HPD-TA

Informacje szczegółowe

Rok publikacji:

2022

Data zatwierdzenia:

2022-03-04

Język danych badawczych:

angielski

Dyscypliny:

nauki fizyczne (Dziedzina nauk ścisłych i przyrodniczych)

DOI:

10.34808/yf83-rg27

Weryfikacja:

Brak weryfikacji

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 174 razy

Wyszukiwarka