The morphology of lead-silicate glasses and nanocomposites doped with iron oxide

Opis

The topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were
annealed at 673K, cooledwith the furnace and polished to the thickness of about 1mm.
The microstructure of all samples was determined by means of atomic forcemicroscopy at their fresh fractureswith the use of NT-MDT Ntegra AFM. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2013.10.008

Plik z danymi badawczymi

set5.zip

48.8 MB, S3 ETag 9ac36337c74924c9fcf73dd00c150978-1, pobrań: 14

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-05

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/fexz-v581

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 58 razy

Wyszukiwarka