The SEM micrographs of the synergistic action between cavitation erosion and pitting corrosion on stainless steel 304

Opis

The dataset contains Scanning Electron Micrographs of stainless steel AISI304 samples made after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected to either cavitation erosion (in deionized water), pitting corrosion (in 8% FeCl3 solution, without cavitation) or cavitation erosion-corrosion (cavitation erosion in 8% FeCl3 solution). The experiment lasted between 5 and 240 min, labeled accordingly, with cyclic cavitation exposure in on/off cycles 30s:30s. The samples were mounted directly underneath the ultrasonic transducer.

Plik z danymi badawczymi

cav_corr.rar
298.5 MB, S3 ETag a81e632b84cf0eff1cbbbfd8ee410a09-1, pobrań: 10
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2020
Data zatwierdzenia:
2020-12-17
Data wytworzenia:
2013
Język danych badawczych:
angielski
Dyscypliny:
  • nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)
  • inżynieria mechaniczna (Dziedzina nauk inżynieryjno-technicznych)
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/805a-h462 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 54 razy