The structure of lead-silicate glasses and nanocomposites doped with iron oxide

Opis

The structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were
annealed at 673K, cooled with the furnace. The presence of crystalline phases was examined by the X-ray diffraction method with the use of a Philips X'Pert Pro MPD system with CuKα radiation. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2013.10.008

Plik z danymi badawczymi

set10.zip

98.6 kB, S3 ETag 4fd68e38f357e50505e6e685631c0193-1, pobrań: 58

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-06

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/sc54-mq90

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 112 razy

Wyszukiwarka