The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials

Opis

The ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA) in a molar ratio equal to 2:1 until a white slurry was obtained. The water-based solution was then added to a titanium precursor mixture and stirred at 80C until fully dissolved. After this, the solution was heated to 150C and condensed until gel was obtained. Next, the gel was transferred into an alumina crucible and calcined for 1 h at 400C, then for 1 h at 600C and finally at 1200C for 12 h under an air atmosphere.

Plik z danymi badawczymi

XRD LSCNiMeT as-prepared.rar

767.6 kB, S3 ETag ecd5a226a05abe417df775991a462585-1, pobrań: 0

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Embargo na plik:: 2026-04-30
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2024

Data zatwierdzenia:

2024-03-11

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/fe9m-yz29

Finansowanie:

Zrozumienie mechanizmów powstawania i kontrolowane wytwarzanie wieloskładnikowych nanometrycznych stopów na aktywnym podłożu do projektowania stabilnych anod dla tlenkowych ogniw paliwowych