X-ray diffraction (XRD) and particle size distribution (PSD) data of iron oxide (Fe3O4) - magnetite particles
Dane BadawczeDataset presenting X-ray diffractogram and particle size distribution of nanomagnetite (Fe3O4) iron oxide particles purchased from Sigma Aldrich (637106).X-ray diffraction study was performed with a PRO X-ray diffractometer (X’Pert PRO Philips diffractometer, Co. Ka radiation, Almelo, Holland), while PSD was determined using laser diffraction technique...
-
Thermgravimetric analysis (TGA) data of cement pastes containing pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeThermogravimetric (TGA) data of cement pastes after 2, 7 and 28 days. Samples designations: Control, BG, BG-A and BG-B are associated with the specimen names in the associated publication.
-
Transmission electron microscope (TEM) and optical microscope images of pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeCollection of raw transmission electron microscope (TEM) micrographs and optical microscope images used in the associated manuscript. All data in accessible *.tif format. Zip package contains:
-
BET specific surface area measurements of bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
X-ray diffraction (XRD) of silica-coated bismuth oxide/gadolinium oxide (Bi2O3+Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
BET specific surface area measurements of silica-coated bismuth oxide (Bi2O3)/gadolinium oxide (Gd2O3) core-shell structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
BET specific surface area measurements of silica-coated bismuth oxide(Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide Bi2O3+Gd2O3 structures
Dane BadawczeExcel (*.xlsx) and Csv (*.csv) files containing raw mechanical (compressive strength) data of cement pastes after 1, 2, 7 and 28 days of curing
-
Isothermal calorimetry data for cement pastes containing pristine Bi2O3/Gd2O3 and silica-coated Bi2O3/Gd2O3 structures
Dane BadawczeCsv file containing raw calorimetric data determined up to 168 h (Tam Air 3 8-channel isothermal calorimeter) of cement pastes containing Bi2O3+Gd2O3 amd silica-coated Bi2O3-Gd2O3 structures. Sample designation in the .csv file is in line with sample designation in the manuscript associated with dataset.
-
Mercury intrusion porosimetry (MIP) results of cement pastes containing Bi2O3/Gd2O3 and silica-coated Bi2O3/Gd2O3 structures
Dane BadawczeMercury intrusion porosimetry (MIP) data - curves of cement pastes containing Bi2O3/Gd2O3 and silica-coated Bi2O3/Gd2O3 structures
-
Rheological properties of cement pastes containing pristine Bi2O3-Gd2O3 and silica coated Bi2O3-Gd2O3 core-shell structures
Dane BadawczeRheological data of cement pastes containing Bi2O3/Gd2O3 particles using MCR 72 (Anton Paar) stress-imposed rheometer, equipped with vane geometry.
-
Mechanical properties of concrete mixes M0-M100 concrete mixes
Dane BadawczeDataset of hardneded properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.Excel file consists results of:
-
Fresh properties of concrete mixes M0-M100 concrete mixes
Dane BadawczeDataset of fresh properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.*. ODS - open-source spreadsheet file file consists results of:
-
Compressive strength and density of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Dane Badawcze*.ODS - open-data source spreadsheet - Dataset presenting:
-
Rheological and compressive strength (ultrasonic pulse method) properties of cement pastes containing iron oxide (Fe3O4) nanoparticles
Dane BadawczeRheological data of cement pastes containing different replacement levels of cement with iron oxide nanoparticles deterimined using MCR 301 (Anton Paar) stress-imposed rheometer, equipped with calibrated helicoidal geometry
-
Raman spectroscopy analysis of synthesized sol-gel silica coatings
Dane BadawczeThese data contains Raman spectra of silica coatings synthesized using sol-gel method A and B, which were described with publication associated with this dataset. Raman scattering was measured with a Renishaw microRaman spectrometer (830 nm).
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
Green strength (buildability performance) of concretes containing magnetite aggregate (M0-M100) mixes
Dane BadawczeRaw data for determination of buildability (green strength) properties of concrete mixes determined by squeezing test using QuantumX MX840B with CATMAN-EASY software, determined after 15, 30, 45 and 60 minutes. Values present force and two displacement measurements by LVDT.Additionally, an Origin (*.opju) file with processed data presenting stress-strain...
-
Sieve analysis of natural and magnetite aggregate
Dane BadawczeSieve analysis of natural river sand and magnetite aggregate used for concrete production
-
Adiabatic calorimetry results for fresh concrete mixes M0 and M100
Dane BadawczeAdiabatic calorimetry results for fresh 3D printed concrete mixes (M0 and M100) determined using Controls S.p.A., Italy calorimeter
-
Thermal conductivity of M0-M100 specimens
Dane BadawczeThermal conductivity and volumetric heat capacity values of M0, M20, M40, M60, M80, M100 samples
-
Mercury intrusion porosimetry (MIP) results of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Dane BadawczeMercury intrusion porosimetry (MIP) data - curves of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite) in *.opju (Origin) format.
-
Isothermal calorimetry data for cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw calorimetric data determined up to 168 h (Tam Air 3 8-channel isothermal calorimeter) of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
Open porosity and oven-dry density of concretes containing magnetite aggregate (M0-M100) mixes
Dane BadawczeRaw data for determination of open porosity and oven-dry densities of concretes containing different amount of magnetite aggregate (M0-M100) mixes. Sample designation is related to the publication associated with dataset.
-
Particle size distribution (laser granulometry) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain raw results of particle size distribution (by volume) of Bi2O3 and Gd2O3 particles determined using a laser diffraction method (Malvern Mastersizer 2000, Worcestershire, UK).
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw mechanical (compressive strength) data of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)