Cavitation wearing of the SUPERSTON alloy after laser treatment at cryogenic conditions

Abstrakt

The purpose of this paper is to demonstrate the method of laser remelting at cryogenic conditions of the SUPERSTON alloy and its influence on microstructure and cavitation wearing. The cavitation test was performed using the rotating disc facility in IPM PAN Gdansk. During the cavitation test, the mass loss of the material with different parameters of laser remelting was determined. Surface and cross-section microstructure of the SUPERSTON alloy after laser treatment and cavitation test were observed by scanning electron microscope. The cavitation resistance of the remelted SUPERSTON alloy was approximately 40% higher in comparison to the base material.

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Solid State Phenomena nr 165, strony 306 - 309,
ISSN: 1012-0394
Język:
angielski
Rok wydania:
2010
Opis bibliograficzny:
Majkowska B., Serbiński W.: Cavitation wearing of the SUPERSTON alloy after laser treatment at cryogenic conditions// Solid State Phenomena. -Vol. 165., (2010), s.306-309
Weryfikacja:
Politechnika Gdańska

wyświetlono 11 razy

Publikacje, które mogą cię zainteresować

Meta Tagi