Centrally Pivoted Tilting Pad Thrust Bearing with Carbon-Based Coated Collar—Experimental Results of Low- and Medium-Speed Operation
Abstrakt
Experimental results of the research on a tilting pad thrust bearing with symmetrical pad support in the conditions of high loads and low speeds are presented in the paper. As described in the literature review, experimental results of tilting pad bearings at low speed/high load regime and transient conditions are rare. Unusual material selection - steel pad against a DLC-type coating on the collar was utilized. Such material combination has been mostly used in automotive industry in concentrated contact friction pairs, but it is not commonly used in thick film contacts. The tests included low speed high load and a test, where a Stribeck curve was reproduced. The steel pads showed minimum traces of contact and no visible wear was noticed on the collar coating. Differences of operation in medium and low speed were observed. Big variations of bearing temperature at medium speed and almost constant pad temperature at low speed were measured. At a specific load of 5 MPa transition to mixed friction was occurring at a sliding speed of approx. 0.18 m/s.
Cytowania
-
9
CrossRef
-
0
Web of Science
-
7
Scopus
Autorzy (3)
-
Wolfgang Braun
- Schaeffler Technologies, GmbH & Co. .
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1080/10402004.2015.1010761
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
TRIBOLOGY TRANSACTIONS
nr 58,
wydanie 5,
strony 882 - 893,
ISSN: 1040-2004 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Wasilczuk M., Wodtke M., Braun W.: Centrally Pivoted Tilting Pad Thrust Bearing with Carbon-Based Coated Collar—Experimental Results of Low- and Medium-Speed Operation// TRIBOLOGY TRANSACTIONS. -Vol. 58, iss. 5 (2015), s.882-893
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1080/10402004.2015.1010761
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 119 razy