Molten salt synthesis method has been used to prepare the single phase magnesium doped lanthanum orthoniobate. The phase composition has been checked by X-ray diffraction method and the microstructure studies have been performed by scanning electron microscopy. The high temperature properties of the material have been investigated by thermogravimetry and electrochemical impedance spectroscopy. A dependence between sample total conductivity and temperature has been found supporting the thesis that there is strong correlation between apparent activation energy of conductivity and structural phase transition at ~500 °C. It has been also shown that the conductivity of magnesium doped lanthanum orthoniobate synthesized by the molten salt route reaches values of ~1 mS/cm at 720°C in wet hydrogen.
Cytowania
-
1 8
CrossRef
-
0
Web of Science
-
1 8
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
CERAMICS INTERNATIONAL
nr 41,
wydanie 6,
strony 7847 - 7852,
ISSN: 0272-8842 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Mielewczyk-Gryń A., Wachowski S., Zagórski K., Jasiński P., Gazda M.: Characterization of magnesium doped lanthanum orthoniobate synthesized by molten salt route// CERAMICS INTERNATIONAL. -Vol. 41, iss. 6 (2015), s.7847-7852
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ceramint.2015.02.121
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 170 razy