he influence of heating and reduction processes on the structural, thermal and mechanical properties of bismuth-silicate glasses has been investigated. Two compositions of glasses: 40Bi2O3–60SiO2 (Bi0.57Si0.43Ox) and 27Bi2O3–73SiO2 (Bi0.43Si0.57Ox) were fabricated by a typical melt quenching technique. Then the reduction in hydrogen at 380 °C for 20, 42 or 67 h was performed. It was found that a 50 μm-thick layer was formed on the glass surface after reduction process. It was confirmed that this layer is formed by granules of metallic bismuth embedded in a glass matrix. The DSC measurements confirmed that melting of metallic bismuth takes place during heating of a previously reduced glass sample. It was also found that heat treatment process influences hardness and Young modulus of Bi–Si–O glass.
Cytowania
-
2 1
CrossRef
-
0
Web of Science
-
2 0
Scopus
Autorzy (8)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF NON-CRYSTALLINE SOLIDS
nr 439,
strony 51 - 56,
ISSN: 0022-3093 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Bochentyn B., Warych A., Szreder N., Mielewczyk-Gryń A., Karczewski J., Prześniak-Welenc M., Gazda M., Kusz B.: Characterization of structural, thermal and mechanical properties of bismuth silicate glasses// JOURNAL OF NON-CRYSTALLINE SOLIDS. -Vol. 439, (2016), s.51-56
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2016.02.026
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 206 razy