Correlation between Fractal Dimension and Areal Surface Parameters for Fracture Analysis after Bending-Torsion Fatigue

Wojciech Macek

doi:10.3390/met11111790

Correlation between Fractal Dimension and Areal Surface Parameters for Fracture Analysis after Bending-Torsion Fatigue

Abstrakt

This paper investigates the fracture surface topography of two steel and aluminum alloys subject to bending-torsion fatigue loadings, as well as their susceptibility to fatigue performance and failure mechanisms. Using fracture surface topography data analysis, elements with different geometries were elaborated. A correlation between the fractal dimension, other selected parameters of surface topography such as areal Sx, and fatigue loading conditions was found. Distinctions in particular regions of cracks were also recognized through proving the correctness and universality of the total fracture surface method. The influence of fatigue loading parameters on the surface to pography of fatigue fractures was demonstrated. For the analyzed cases, results show that the frac tal dimension and standard surface topography parameters represent a correlation between them and loading conditions. As a single parameter, the appropriate loading ratio cannot be outright calculated with fractal dimension, but can be estimated with some approximation, taking into ac count additional assumptions.

Cytowania

2 4

CrossRef
0

Web of Science
2 5

Scopus

Autor (1)

Wojciech Macek dr hab. inż.

Cytuj jako

Pełna treść

pobierz publikację

pobrano 54 razy

Wersja publikacji: Accepted albo Published Version
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met11111790
Licencja: otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuły w czasopismach
Opublikowano w:: Metals nr 11,
ISSN: 2075-4701
Język:: angielski
Rok wydania:: 2021
Opis bibliograficzny:: Macek W.: Correlation between Fractal Dimension and Areal Surface Parameters for Fracture Analysis after Bending-Torsion Fatigue// Metals -Vol. 11,iss. 11 (2021), s.1790-
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/met11111790
Weryfikacja:: Politechnika Gdańska