Corrigendum to “Fatigue life improvement using low transformation temperature weld material with measurement of residual stress” [Int. J. Fatigue 164 (2022) 107137]
Abstrakt
Welding processes often produce high levels of tensile residual stress. Low transformation temperature (LTT) welding wires utilise phase transformation strains to overcome the thermal contraction of a cooling weld. In this paper, the residual stress within each weld was quantified using the milling/strain gauge method, being the strain change measured as the weldment was milled away. The fatigue tests were conducted under uniaxial loading considering two types of LTT materials. The results show that the crack propagation of all samples was similar in cycles although both LTT materials extended the crack initiation, and, therefore, the overall life of the part. It was found that both LTT materials reduced the residual tensile stresses, increased the residual compressive stresses, leading to increase in fatigue life about 30%.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (6)
-
Jordan Franks
-
Greg Wheatley
-
Pedram Zamani
-
Reza Masoudi Nejad
-
Ricardo Branco
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
INTERNATIONAL JOURNAL OF FATIGUE
nr 183,
ISSN: 0142-1123 - Język:
- angielski
- Rok wydania:
- 2024
- Opis bibliograficzny:
- Franks J., Wheatley G., Zamani P., Nejad R. M., Macek W., Branco R.: Corrigendum to “Fatigue life improvement using low transformation temperature weld material with measurement of residual stress” [Int. J. Fatigue 164 (2022) 107137]// INTERNATIONAL JOURNAL OF FATIGUE -, (2024), s.108260-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ijfatigue.2024.108260
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 50 razy
Publikacje, które mogą cię zainteresować
Fatigue life improvement using low transformation temperature weld material with measurement of residual stress
- J. Franks,
- G. Wheatley,
- P. Zamani
- + 4 autorów
An investigation on residual stress and fatigue life assessment of T-shape welded joints
- F. Samadi,
- J. Mourya,
- G. Wheatley
- + 4 autorów
Corrigendum to “An investigation on residual stress and fatigue life assessment of T-shape welded joints” [Eng. Fail. Anal. 141 (2022) 106685]
- J. Mourya,
- G. Wheatley,
- M. Nizam Khan
- + 3 autorów
The effect of elevated temperature on LCF damage growth in 2024AA – Experiment and modeling
- A. Falkowska,
- A. Tomczyk,
- A. Seweryn