Bioactive glasses have recently been extensively used to replace, regenerate, and repair hard tissues in the human body because of their ability to bond with living tissue. In this work, the effects of replacing Na2O with MgO on the electrical, biosolubility, and thermal properties of the target glass 10Na2O–60P2O5–30CaO (in mol%) were investigated. The electrical properties of the glasses were studied with the impedance spectroscopy technique. At 473 K, DC conductivity values decreased from 4.21*10−11 to 4.21*10−12 S cm−1 after complete substitution of MgO for Na2O. All samples had a similar activation energy of the DC conduction process ~1.27 eV. Conduction mechanisms were found to be due to hop of ions: Na+, Mg2+, and probable H+. FTIR analysis showed that, as the Mg content increased, the Q2 unit (PO2‐) shifted towards higher wavenumbers. The proportion of Q3 unit (P2O5) decreased in the glass structure. This confirmed that the replacement of Na+ by Mg2+ was accompanied by concurrent polymerization of the calcium–phosphate glass network. The biosolubility test in the phosphate‐buffered saline solution showed that the magnesium addition enhanced the biosolubility properties of Na2O–CaO–P2O5 glasses by increasing their dissolution rate and supporting forming CaP‐rich layers on the surface. The glass transition temperature increased, and thermal stability decreased substantially upon substitution of Na2O by MgO.
Cytowania
-
7
CrossRef
-
0
Web of Science
-
7
Scopus
Autorzy (6)
-
Sharafat Ali profesor
-
Bo Jonson profesor
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma14102626
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 14,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Wójcik N., Ali S., Karczewski J., Jonson B., Bartmański M., Barczyński R.: DC and AC Conductivity, Biosolubility and Thermal Properties of Mg-Doped Na2O–CaO–P2O5 Glasses// Materials -Vol. 14,iss. 10 (2021), s.2626-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma14102626
- Źródła finansowania:
-
- IDUB
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
wyświetlono 158 razy
Publikacje, które mogą cię zainteresować
Synthesis, thermal, structural and electrical properties of vanadium-doped lithium-manganese-borate glass and nanocomposites
- A. Jarocka,
- P. Michalski,
- J. Ryl
- + 3 autorów