Glass/polyester laminate coated with gelcoat layer of different thickness 0,5; 1,5; 3 mm was studied in terms of blistering behaviour and water sorption in hot water environment. Blistering was found to be accelerated for thin (0,5 mm) gel-coat layer compared to the thick (1,5; 3 mm), however no significant difference in blistering behaviour was observed between the laminates with gel-coat thickness 1,5 and 3 mm which may suggest that increasing the gel-coat thickness is effective only to a certain thickness limit. Microscopic studies demonstrated that blistering behaviour was related to the formation of subsurface cracks - longer and less densely distributed in thin gel-coat layers in contrast to numerous small cracks formed in the thick gel-coats.
Autorzy (3)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Solid State Phenomena
nr 183,
strony 107 - 110,
ISSN: 1012-0394 - Język:
- angielski
- Rok wydania:
- 2012
- Opis bibliograficzny:
- Landowski M., Budzik M., Imielińska K.: Degradation of Gel-Coat Layer in Glass/Polyester Laminate in Seawater Environment// Solid State Phenomena. -Vol. 183., (2012), s.107-110
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 115 razy