Effect of kenaf fibre modification on morphology and mechanical properties of thermoplastic polyurethane materials

Abstrakt

The presented study examined the morphology and mechanical properties of biocomposites obtained from kenaf natural fibre and thermoplastic polyurethane. Kenaf was modified using various methods, namely: acetylation, blocked isocyanate, maleic anhydride and permanganate treatment. Those methods and ways of carrying out of surface modifications were not studied before on kenaf/thermoplastic polyurethane composites. Different fibre loadings: 10% and 30% (by weight) were applied. The chemical treatments of fibres was confirmed by FTIR. The fibres surface and adhesion of the fibres to matrix was investigated using a scanning electron microscope (SEM). The modulus, tensile strength, elongation at break, hardness, resilience and water absorption were also determined; all results were compared with a untreated kenaf fibre composite. SEM investigations of fibres showed the differences of fibre surface after the chemical treatment. A good adhesion between the polymer matrix and fibres was observed for PU/PMn-KF 30 sample. DMA results indicated that the greatest values exhibited samples with fibre treated by acetylation and permanganate treatment. Increasing the amount of fillers in the polymer matrix leads to higher hardness values and water uptake. Tensile strength and resilience of composites decreased when a higher proportion of kenaf fibre was added. It was observed that the treated fibre composites showed improvement in tensile properties, hardness, resilience and lower water uptake for composites with 10% fibre loading.

Cytowania

  • 5 4

    CrossRef

  • 5 4

    Web of Science

  • 6 1

    Scopus

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
INDUSTRIAL CROPS AND PRODUCTS nr 74, strony 566 - 576,
ISSN: 0926-6690
Język:
angielski
Rok wydania:
2015
Opis bibliograficzny:
Datta J., Kopczyńska P.: Effect of kenaf fibre modification on morphology and mechanical properties of thermoplastic polyurethane materials// INDUSTRIAL CROPS AND PRODUCTS. -Vol. 74, (2015), s.566-576
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.indcrop.2015.05.080
Weryfikacja:
Politechnika Gdańska

wyświetlono 46 razy

Publikacje, które mogą cię zainteresować

Meta Tagi