Evaluation of adhesion strength, corrosion, and biological properties of the MWCNT/TiO2 coating intended for medical applications
Abstrakt
Multi-wall carbon nanotube (MWCNT) coatings are gaining increasing interest because of their special properties used in many science fields. The titania coatings are known for their improvement of osteoblast adhesion, thus changing the surface architecture. Bi-layer coatings comprising 0.25 wt% of the MWCNTs and 0.30 wt% of titania (anatase structure) were synthesized in a two-stage procedure using the electrophoretic deposition method (EPD). The MWCNT and TiO2 coatings were deposited with voltage and time parameters, respectively, of 20 V and 0.5 min, and 50 V and 4 min. EDS, AFM, SEM, Raman spectroscopy, nano-scratch test, potentiodynamic corrosion tests, wettability studies, and cytotoxicity determined with MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) test on human dermal fibroblasts (HDF) and mouse osteoblast precursors (MC3T3), and lactate dehydrogenase (LDH) activity test were carried out on examined surfaces. The prepared MWCNT/TiO2 coating is uniformly distributed by MWCNTs and agglomerated by TiO2 particles of size ranging from 0.1 to 3 mm. Raman spectroscopy confirmed the anatase structure of the TiO2 addition and showed typical peaks of the MWCNTs. The MWCNT/TiO2 coating had higher roughness, higher adhesion strength, and improved corrosion resistance compared to the MWCNT basic coating. The results of biological tests proved that physicochemical properties of the surface, such as high porosity and wettability of MWCNT/TiO2-coated material, would support cell adhesion, but toxic species could be released to the culture medium, thus resulting in a decrease in proliferation.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (5)
-
Katarzyna Roszek dr hab.
-
Malwina Liszewska
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/d3ra05331h
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
RSC Advances
nr 13,
strony 30108 - 30117,
ISSN: 2046-2069 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Rogala-Wielgus D., Majkowska-Marzec B., Zieliński A., Roszek K., Liszewska M.: Evaluation of adhesion strength, corrosion, and biological properties of the MWCNT/TiO2 coating intended for medical applications// RSC Advances -Vol. 13,iss. 43 (2023), s.30108-30117
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/d3ra05331h
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 23 razy