Experimental and Numerical Investigation of Tensile and Flexural Behavior of Nanoclay Wood-Plastic Composite
Abstrakt
In this study, the effect of wood powder and nanoclay particle content on composites’ mechanical behavior made with polyethylene matrix has been investigated. The wood flour as a reinforcer made of wood powder was at levels of 30, 40, and 50 wt.%, and additional reinforcement with nanoclay at 0, 1, 3, and 5 wt.%. Furthermore, to make a composite matrix, high-density polyethylene was used at levels of 70, 60, and 50% by weight. Wood-plastic composite (WPC) specimens were manufactured in injection molding. After preparing the specimens, tensile and bending tests were performed on samples. The mechanical properties such as tensile and flexural strength and flexural modulus were measured. Results showed that nanoclay particle content increases flexural modulus, flexural strength, modulus of elasticity, and tensile strength. The experimental test results show that Young’s moduli increased with the volume of wood flour. The biggest modulus of elasticity was achieved in the samples having 50 wt.% of wood powder. Furthermore, the highest value of tensile strength was achieved at the level of 30 wt.%. The highest flexural strength was for the sample containing 50% wood powder by weight. Additionally, a numerical model was made utilizing the Abaqus software using the finite element method (FEM). Comparing the numerical and experimental results, it was found that they are compatible in the linear-elastic and plastic state of the material. There are no crucial differences between experiment and FEM.
Cytowania
-
6
CrossRef
-
0
Web of Science
-
7
Scopus
Autorzy (5)
-
M. E. Golmakani Dr.
- Islamic Azad University, Mashhad 1584743311, Iran
-
Seyed M. Mahoori MSc
- Islamic Azad University, Mashhad 1584743311, Iran
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 14,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Golmakani M. E., Wiczenbach T., Malikan M., Mahoori S. M., Eremeev V.: Experimental and Numerical Investigation of Tensile and Flexural Behavior of Nanoclay Wood-Plastic Composite// Materials -Vol. 14,iss. 11 (2021), s.2773-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma14112773
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 161 razy
Publikacje, które mogą cię zainteresować
Optimization of biocorrosion resistance and mechanical properties of PM Ti–XAl–2Fe–3Cu alloys by response surface methodology
- M. Najafizadeh,
- M. Ghasempour-Mouziraji,
- M. Hosseinzadeh
- + 6 autorów
Thermomechanical and Fire Properties of Polyethylene-Composite-Filled Ammonium Polyphosphate and Inorganic Fillers: An Evaluation of Their Modification Efficiency
- M. Barczewski,
- A. Hejna,
- K. Sałasińska
- + 4 autorów