Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens

Abstrakt

The objectives of this study were to investigate the fracture surface topography of X8CrNiS18-9 austenitic stainless-steel specimens for different loadings and notch radii and to supplement the knowledge about the fracture mechanisms for fatigue performance. Cases with three different values of the notch radius ρ and the stress amplitude σa were analysed. The fracture topographies were quantified by the areas over their entire surfaces with the aid of an optical confocal measurement system. The results showed a well-correlated root mean square height Sq and void volume Vv, identifying the characteristics of the entire fracture method. A fracture surface topography fatigue damage model was developed based on the product of the stress amplitude σa by the Sq to the Vv ratio. Overall, the predictions were close to the fatigue lives found in the experiments.

Cytowania

  • 1 9

    CrossRef

  • 0

    Web of Science

  • 1 9

    Scopus

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
ENGINEERING FAILURE ANALYSIS nr 135,
ISSN: 1350-6307
Język:
angielski
Rok wydania:
2022
Opis bibliograficzny:
Macek W., Robak G., Żak K., Branco R.: Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens// ENGINEERING FAILURE ANALYSIS -Vol. 135, (2022), s.106121-
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.engfailanal.2022.106121
Źródła finansowania:
  • COST_FREE
Weryfikacja:
Politechnika Gdańska

wyświetlono 74 razy

Publikacje, które mogą cię zainteresować

Meta Tagi