The growth and characterization of CePtIn4, stabilized by 10% Zn substitution for In, is reported. The new material is orthorhombic, space group Cmcm (No. 63), with lattice parameters a = 4.51751(4) Å, b = 16.7570(2) Å, and c = 7.36682(8) Å, and the refined crystal composition has 10% of Zn substituted for In, i.e., the crystals are CePt(In0.9Zn0.1)4. Crystals were grown using a self-flux method: only growths containing Zn yielded CePtIn4 crystals, while Ce3Pt4In13 crystals formed when Zn was not present. Anisotropic temperature-dependent magnetic susceptibilities for single crystals show that Zn-stabilized CePtIn4 orders magnetically at ∼1.9 K. High-temperature Curie–Weiss fits indicate an effective moment of ∼2.49 μB/Ce and a directionally averaged Weiss-temperature of approximately −31 K. Specific heat data shows a peak consistent with the ordering temperature seen in the magnetic susceptibility data. Zn-stabilized CePtIn4 is metallic and displays no superconducting transition down to 0.14 K.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (9)
-
Elizabeth M. Carnicom
- Department of Chemistry, Princeton University -
-
Fabian von Rohr
- Department of Chemistry, Princeton University -
-
Tai Kong
- Department of Chemistry, Princeton University -
-
Karoline Stolze
- Department of Chemistry, Princeton University -
-
Weiwei Xie
- Department of Chemistry, Louisiana State University -
-
Satya Kushwaha
- Department of Chemistry, Princeton University -
-
Robert J. Cava
- Department of Chemistry, Princeton University -
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.7566/JPSJ.86.084710
- Licencja
- Copyright (2017 The Physical Society of Japan)
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN
nr 86,
wydanie 8,
strony 1 - 5,
ISSN: 0031-9015 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Carnicom E., Klimczuk T., Rohr F., Winiarski M., Kong T., Stolze K., Xie W., Kushwaha S., Cava R.: Growth, Crystal Structure and Magnetic Characterization of Zn-Stabilized CePtIn4// JOURNAL OF THE PHYSICAL SOCIETY OF JAPAN. -Vol. 86, iss. 8 (2017), s.1-5
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.7566/jpsj.86.084710
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 147 razy