High Temperature Corrosion Evaluation of Porous Hastelloy X Alloy in Air and Humidified Hydrogen Atmospheres
Abstrakt
In this work a commercially available porous Hastelloy X alloy is characterized in terms of high temperature corrosion resistance. The alloy was oxidized in the temperature range from 500C to 900C in air and humidified hydrogen for 100 hours. Corrosion rates and porosity changes were measured. Microstructural characterization was performed using X-ray diffractometry and scanning electron microscopy. Results show that porous alloys oxidize rapidly even for the relatively short time of the study. Long term operation in fuel cell conditions seems feasible especially in hydrogen atmosphere at temperatures preferably not exceeding 700C.
Cytowania
-
6
CrossRef
-
0
Web of Science
-
8
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF THE ELECTROCHEMICAL SOCIETY
nr 163,
wydanie 6,
strony 296 - 302,
ISSN: 0013-4651 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Molin S., Dunst K., Karczewski J., Jasiński P.: High Temperature Corrosion Evaluation of Porous Hastelloy X Alloy in Air and Humidified Hydrogen Atmospheres// JOURNAL OF THE ELECTROCHEMICAL SOCIETY. -Vol. 163, iss. 6 (2016), s.296-302
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1149/2.0741606jes
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 138 razy
Publikacje, które mogą cię zainteresować
THE ROLE OF THIN FUNCTIONAL LAYERS IN SOLID OXIDE FUEL CELLS
- S. Molin,
- A. Chrzan,
- J. Karczewski
- + 2 autorów
2016
Developing high-performance oxygen electrodes for intermediate solid oxide cells (SOC) prepared by Ce0.8Gd0.2O2−δ backbone infiltration
- Ö. F. Aksoy,
- B. Lemieszek,
- M. Murutoglu
- + 3 autorów
2024