Highly stable CsFAPbIBr perovskite solar cells with dominant bulk recombination at real operating temperatures
Abstrakt
Mixed-cation mixed-halide perovskite solar cells have been characterized in DC at different temperatures (from −20 °C up to 50 °C) and the time evolution of the device efficiency has been assessed using different degradation protocols (indoors and outdoors). The completely planar p–i–n structure is ITO/CuNiOx/PTAA/CsFAPbIBr/PCBM/PEI/Ag. Pristine current–voltage characteristics barely show hysteresis, at any temperature. Open circuit voltage decreases with temperature at a rate of −1.5 mV °C−1, and the obtained PCE temperature coefficient is lower than −0.001% K−1, which is an outstanding value for this emerging photovoltaic technology. Cells have been degraded under different protocols: indoors using different light/dark cycles and outdoors in a high temperature and high irradiation location. Cells show no significant decrease of the efficiency after more than 350 h of indoor light cycling and the estimated T80 obtained for the sample degraded outdoors under high irradiation and high temperature conditions is ∼15 days.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (9)
-
Beatriz Romero Prof
-
Silvia Delgado
-
Cheng-Tsung Chang
-
Gonzalo Del Pozo
-
Belén Arredondo
-
Diego Martín-Martín
-
Pedro Contreras
-
Yulia Galagan dr
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.34808/m46x-ym10
- Licencja
- Copyright (2023 Royal Society of Chemistry)
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Sustainable Energy & Fuels
nr 7,
strony 2146 - 2152,
ISSN: 2398-4902 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Romero B., Delgado S., Głowienka D., Chang C., Del Pozo G., Arredondo B., Martín-Martín D., Contreras P., Galagan Y.: Highly stable CsFAPbIBr perovskite solar cells with dominant bulk recombination at real operating temperatures// Sustainable Energy & Fuels -Vol. 7,iss. 9 (2023), s.2146-2152
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/d2se01766k
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 88 razy
Publikacje, które mogą cię zainteresować
Quantitative loss analysis of opaque perovskite solar cells using transient and steady-state characterization
- K. Cudo,
- R. Ollearo,
- G. H. Gelinck
- + 2 autorów
Understanding the Electronic Structure and Optical Properties of Vacancy-Ordered Double Perovskite A2BX6 for Optoelectronic Applications
- M. Faizan,
- X. Wang,
- S. A. M. Abdelmohsen
- + 7 autorów
Effect of Different Bromine Sources on the Dual Cation Mixed Halide Perovskite Solar Cells
- D. Głowienka,
- F. Giacomo Di,
- M. Najafi
- + 5 autorów
Spray deposited carbon nanotubes counter electrodes for dye-sensitized solar cells
- K. SiuzdaK,
- M. Klein,
- M. Sawczak
- + 4 autorów