Impact behaviour of glass fibre /epoxy composites with nano- SiO2 modified resin was studied in terms of low velocity impact after water exposure. Nanocomposites with 1%, 2%, 3% 5% 7% nano-SiO2 (Nanopox- Evonic) were investigated. Peak impact load and impact damage area as a function of nanoparticle contents were compared for dry specimens and for samples exposed to water (0.7 %wt. 1.7% water absorbed) at 1J, 2J 3J impact energies. For unmodified composite peak force was higher than for 3% modified specimens and higher for dry specimens than those exposed to water. Impact damage areas were plotted as a function of water contents for modified and unmodified samples. Failure modes were illustrated using SEM micrographs. Numeropus matrix cracks were the dominating failure mode in dry speciemens both unmodified and the modified. Fibre fracture was observed at 3J impact energy in all dry unmodified samples, however water exposure prevented early fibre fracture in nanocomposites. The proposed energy absorption mechanism is nanoparticles debonding.
Cytowania
-
3
CrossRef
-
0
Web of Science
-
0
Scopus
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/adms-2015-0010
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Advances in Materials Science
nr 15,
wydanie 2,
strony 30 - 35,
ISSN: 1730-2439 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Landowski M., Imielińska K.: Impact Behaviour of Glass Fribre /Epoxy Composites with Nano-Enhanced Resin after Water Exposure// Advances in Materials Science. -Vol. 15., iss. 2 (2015), s.30-35
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1515/adms-2015-0010
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 131 razy
Publikacje, które mogą cię zainteresować
Impact performance of novel multi-layered prepacked aggregate fibrous composites under compression and bending
- G. Murali,
- S. R. Abid,
- Y. M. Amran
- + 4 autorów
Mechanical Properties of Bio-Composites Based on Epoxy Resin and Nanocellulose Fibres
- M. Roszowska-Jarosz,
- J. Masiewicz,
- M. Kostrzewa
- + 4 autorów