Impedance monitoring of corrosion degradation of plasma electrolytic oxidation coatings (PEO) on magnesium alloy

Abstrakt

Impedance technique based on continuous multisinusoidal current perturbation was used to explain degradation process of plasma electrolytic oxidation coatings (PEO) on magnesium alloy. An obtained impedance spectrum was fitted by electrical equivalent circuit to describe properties of conversion layer on magnesium alloy. Additionally, galvanostatic mode maintained during experiment, with DC current equal to zero, allowed to achieve corrosion potential in degradation process. This methodology has advantage over more conventional methods. It allows observing parameters change in function of time and explanation of the degradation process of PEO on magnesium alloy.

Cytowania

  • 1 7

    CrossRef

  • 1 7

    Web of Science

  • 1 8

    Scopus

Autorzy (5)

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
JOURNAL OF ALLOYS AND COMPOUNDS nr 722, strony 406 - 413,
ISSN: 0925-8388
Język:
angielski
Rok wydania:
2017
Opis bibliograficzny:
Gaweł Ł., Nieuzyla L., Nawrat G., Darowicki K., Ślepski P.: Impedance monitoring of corrosion degradation of plasma electrolytic oxidation coatings (PEO) on magnesium alloy// JOURNAL OF ALLOYS AND COMPOUNDS. -Vol. 722, (2017), s.406-413
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jallcom.2017.06.120
Weryfikacja:
Politechnika Gdańska

wyświetlono 49 razy

Publikacje, które mogą cię zainteresować

Meta Tagi