Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses
Abstrakt
The effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some granules of metallic bismuth with a diameter of tens to hundreds of nanometers were formed on the surface of the glass. Furthermore, depletion of lead was observed in these samples in relation to the initial stoichiometry of the glass prior to trial reduction.
Cytuj jako
Pełna treść
pobierz publikację
pobrano 28 razy
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Technical Issues
nr 2,
strony 3 - 8,
ISSN: 2392-3954 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Bochentyn B.: Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses// Technical Issues. -Vol. 2., (2015), s.3-8
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 113 razy
Publikacje, które mogą cię zainteresować
Properties of Composite Oxide Layers on The Ti13Nb13Zr Alloy
- A. Ossowska,
- R. Beutner,
- D. Scharnweber
- + 1 autorów
2017