Low temperature processed MnCo2O4 and MnCo1.8Fe0.2O4 as effective protective coatings for solid oxide fuel cell interconnects at 750 °C
Abstrakt
In this study two materials, MnCo2O4 and MnCo1.8Fe0.2O4 are studied as potential protective coatings for Solid Oxide Fuel Cell interconnects working at 750 °C. First powder fabrication by a modified Pechini method is described followed by a description of the coating procedure. The protective action of the coating applied on Crofer 22 APU is evaluated by following the area specific resistance (ASR) of the scale/coating for 5500 h including several thermal cycles. The coating is prepared by brush painting and has a porous structure after deposition. Post mortem microstructural characterization performed on the coated samples shows good protection against chromium diffusion from the chromia scale ensured by a formation of a dense reaction layer. This study shows, that even without high temperature sintering and/or reactive sintering it is possible to fabricate protective coatings based on MnCo spinels.
Cytowania
-
6 7
CrossRef
-
0
Web of Science
-
6 8
Scopus
Autorzy (6)
-
Sebastian Molin
- Technical University of Denmark Department of Energy Conversion and Storage
-
Lars Mikkelsen
- Technical University of Denmark Department of Energy Conversion and Storage
-
W. Zhang
- Technical University of Denmark Department of Energy Conversion and Storage
-
Ming Chen
- Technical University of Denmark Department of Energy Conversion and Storage
-
Peter Vang Hendriksen
- Technical University of Denmark Department of Energy Conversion and Storage
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF POWER SOURCES
nr 336,
strony 408 - 418,
ISSN: 0378-7753 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Molin S., Jasiński P., Mikkelsen L., Zhang W., Chen M., Hendriksen P.: Low temperature processed MnCo2O4 and MnCo1.8Fe0.2O4 as effective protective coatings for solid oxide fuel cell interconnects at 750 °C// JOURNAL OF POWER SOURCES. -Vol. 336, (2016), s.408-418
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jpowsour.2016.11.011
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 73 razy
Publikacje, które mogą cię zainteresować
Ceria Based Protective Coatings for Steel Interconnects Prepared by Spray Pyrolysis
- D. Grudzień,
- M. Chen,
- S. Molin
- + 2 autorów
High temperature oxidation behavior of SUS430 SOFC interconnects with Mn-Co spinel coating in air
- C. Jia,
- Y. Wang,
- S. Molin
- + 3 autorów