Mechanical and structural behavior of high-strength low-alloy steel pad welded by underwater wet welding conditions
Abstrakt
The aim of the paper was to determine the metallurgical and mechanical behaviors of a high-strength low-alloy (HSLA) steel pad-welded specimen used in the structures of industrial and naval parts. Then to predict the metallurgical consequences (nature of the phases present) and the mechanical properties (hardness and impact strength) of the pad-welded steel obtained by underwater wet welding with different heat input values. The XRD patterns clearly reveal a ferritic alpha steel S460N for both parameters. The ferritic quantification is above 70 wt% for low-alloy steel. The welded specimens are characterized by the presence of different phases. In a specimen performed with higher heat input, the complex oxide Mn2TiO4 was found to be around 7 wt%. Moreover, the solid solution formed with iron and manganese was observed. The hardness results obtained by indentation showed that the higher heat input resulted in higher hardness values (54 HRC) than for specimen performed with lower parameters (45 HRC). The impact test showed that the toughness of both pad-welded layers is greater than the toughness of the base material (40 kV for S2 and 34 kV for S1 about 27 kV for low-alloy steel). Moreover, it was observed that higher heat input results in increasing the impact strength of pad welds.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (4)
-
Rassim Younes Dr.
- Université de Bejaia, Algieria
-
Idir Abdelhak Dr.
- Université de Bejaia, Algieria
-
Mohand Amokrane Bradai Prof.
- Université de Bejaia, Algieria
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s00170-023-12681-7
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY
nr 129,
strony 5615 - 5624,
ISSN: 0268-3768 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Younes R., Tomków J., Abdelhak I., Bradai M. A.: Mechanical and structural behavior of high-strength low-alloy steel pad welded by underwater wet welding conditions// INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY -,iss. 129 (2023), s.5615-5624
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s00170-023-12681-7
- Źródła finansowania:
-
- Działalność statutowa/subwencja
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 66 razy
Publikacje, które mogą cię zainteresować
Bead-on-Plate Underwater Wet Welding on S700MC Steel
- J. Tomków,
- A. Świerczyńska,
- M. Landowski
- + 2 autorów