Mechanical Properties and Wear Susceptibility Determined by Nanoindentation Technique of Ti13Nb13Zr Titanium Alloy after “Direct Laser Writing”
Abstrakt
Laser treatment has often been applied to rebuild the surface layer of titanium and its alloys destined for long-term implants. Such treatment has always been associated with forming melted and re-solidified thin surface layers. The process parameters of such laser treatment can be different, including the patterning of a surface by so-called direct writing. In this research, pulse laser treatment was performed on the Ti13Nb13Zr alloy surface, with the distance between adjacent laser paths ranging between 20 and 50 µm. The obtained periodic structures were tested to examine the effects of the scan distance on the microstructure using SEM, the roughness and chemical and phase composition using EDS and XRD, and the mechanical properties using the nanoindentation technique. After direct laser writing, the thickness of the melted layers was between 547 and 123 µm, and the surface roughness varied between 1.74 and 0.69 µm. An increase in hardness was observed after laser treatment. The highest hardness, 5.44 GPa, was obtained for the sample modified with a laser beam spacing of 50 µm. The value of the distance has been shown to be important for several properties and related to a complex microstructure of the thin surface layer close to and far from the laser path.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (7)
-
Roman Ostrowski
-
Jean-marc Olive Dr hab.
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma16134834
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 16,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Jażdżewska M., Majkowska-Marzec B., Zieliński A., Ostrowski R., Frączek A., Karwowska G., Olive J.: Mechanical Properties and Wear Susceptibility Determined by Nanoindentation Technique of Ti13Nb13Zr Titanium Alloy after “Direct Laser Writing”// Materials -,iss. 13 (2023), s.4834-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma16134834
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 103 razy