The structure, optical and electrical properties of manganese borosilicate glasses of the composition xMnO–(80 − x)SiO 2 –20B 2 O 3 (x = 40, 50, and 60 mol%) were investigated. The dependence of the glass structure on its composition was discussed and related to electrical properties. A separation of two amorphous phases was observed. It was suggested that one phase is MnO-rich and the other is SiO 2 -rich. It was found that the conductivity of MnO-rich phase is much higher than the conductivity of the other phase. The analysis of the valence states of manganese suggest that the transition metal ions are mainly present at second oxidation state. Magnetic susceptibility measurements show antiferromagnetic interactions in samples.
Cytowania
-
1 9
CrossRef
-
0
Web of Science
-
2 1
Scopus
Autorzy (7)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF NON-CRYSTALLINE SOLIDS
nr 432-424,
strony 68 - 75,
ISSN: 0022-3093 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Kupracz P., Karczewski J., Prześniak-Welenc M., Szreder N., Winiarski M., Klimczuk T., Barczyński R.: Microstructure and electrical properties of manganese borosilicate glasses// JOURNAL OF NON-CRYSTALLINE SOLIDS. -Vol. 432-424, (2015), s.68-75
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jnoncrysol.2015.05.014
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 202 razy