Moisture content during and after high- and normal-temperature drying processes of wood

Abstrakt

The aim of the article is to present the results of moisture content of wood during and after the high-temperature steam and air–steam mixture drying processes and after an open air-drying process. The knowledge of moisture content changes of wood in the process of its drying is one of the important parameters to economy drying process and to keep the quality of dried wood. Wood samples, namely, spruce (Picea abies K.) and beech (Fagus silvatica L.) from the northern part of Poland, were subject to steam, air–steam mixture and, air-drying, respectively, with a temperatures about 105, 80, and 25°C. The samples of thickness 70 mm and length about 1,050 of spruce, and about 1,500 mm of beech were used. They were machined by the modern narrow kerf frame sawing machine. Temperature of the cross section of dried wood was measured by thermocouples, wood moisture content was determined during process using moisture sensors. Measurements of moisture content for steam-dried and air-dried samples, as reference, allowed to reveal the effect of drying process on moisture content of wood. It has been recognized that steam wood drying causes almost constant amount of moisture in treated material in comparison to air-drying one.

Cytowania

  • 1 1

    CrossRef

  • 1 6

    Web of Science

  • 1 8

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
DRYING TECHNOLOGY nr 36, wydanie 6, strony 751 - 761,
ISSN: 0737-3937
Język:
angielski
Rok wydania:
2018
Opis bibliograficzny:
Barański J.: Moisture content during and after high- and normal-temperature drying processes of wood// DRYING TECHNOLOGY. -Vol. 36, iss. 6 (2018), s.751-761
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1080/07373937.2017.1355319
Źródła finansowania:
  • Obróbka termiczna drewna podczas suszenia wysokotemperaturowego parą przegrzaną lub mieszaniną parowo-gazową 6298/B/T02/2011/40
Weryfikacja:
Politechnika Gdańska

wyświetlono 57 razy

Publikacje, które mogą cię zainteresować

Meta Tagi