Morphology and local chain structure of polyamide 6 modified in the solid state with a semi-aromatic nylon salt - Publikacja - MOST Wiedzy

Wyszukiwarka

Morphology and local chain structure of polyamide 6 modified in the solid state with a semi-aromatic nylon salt

Abstrakt

Structural and conformational differences between the polyamide 6 (PA6) homopolymer and two copolymers of PA6 modified in the solid state with 20 and 30 wt% of the semi-aromatic nylon salt of 1,5-diamino-2-methylpentane (Dytek A) and isophthalic acid (IPA) in the feed were investigated. Room temperature wide-angle X-ray diffraction (WAXD) analysis together with 13C{1H} cross-polarization/magic-angle spinning solid-state (CP/MAS) NMR and 2D 13C{1H} FSLG-HETCOR experiments showed that there is no co-crystallization of the Dytek A-isophthalic acid (DyI) salt with the PA6 repeat units. A steady decrease of the degrees of crystallinity with increasing amount of the incorporated DyI salt was proven. Upon heating of the samples a transformation of trans conformers into gauche conformers of the polymer chain fragments was observed both by performing temperature-dependent FT-IR and solid-state NMR experiments.

Cytowania

  • 3

    CrossRef

  • 4

    Web of Science

  • 3

    Scopus

Autorzy (5)

Słowa kluczowe

Pełna treść

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
publikacja w in. zagranicznym czasopiśmie naukowym (tylko język obcy)
Opublikowano w:
Materials Today Communications nr 2, strony 62 - 69,
ISSN: 2352-4928
Język:
angielski
Rok wydania:
2015
Opis bibliograficzny:
Cakir S., Jasińska-Walc L., Villani M., Hansen M., Koning C.. Morphology and local chain structure of polyamide 6 modified in the solid state with a semi-aromatic nylon salt. Materials Today Communications, 2015, Vol. 2, , s.62-69
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.mtcomm.2014.12.002
Weryfikacja:
Politechnika Gdańska

wyświetlono 15 razy

Publikacje, które mogą cię zainteresować

Meta Tagi