Morphology and properties of nanotubular oxide layer on the Ti13Zr13Nb alloy

Abstrakt

The Ti13Zr13Nb alloy in solid and porous form was oxidised. The constant voltage 20 V, oxidation time 0.5 and 1 h, and 1 M H3PO4 (orthophosphoric acid) with addition of HF (hydrofluoric acid) as a test solution were applied. SEM (Scanning Electron Microscope) examinations of surface, EDS (Energy Dispersive X-ray Spectroscopy) chemical analysis, nanohardness and nano-scratch tests, and corrosion potentiokinetic tests at various pH were performed. The results show that oxidation of this ternary alloy in acidic solution in presence of fluoride ions results in an appearance of nanotubular oxide layer of high nanohardness, well adjacent to the base but relatively easily damaged in scratch test. Different colonies of nanotubes are observed, related to different phases of the alloy.

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
SURFACE & COATINGS TECHNOLOGY nr 258, strony 1239 - 1248,
ISSN: 0257-8972
Język:
angielski
Rok wydania:
2014
Opis bibliograficzny:
Ossowska A., Sobieszczyk S., Supernak-Marczewska M., Zieliński A.: Morphology and properties of nanotubular oxide layer on the Ti13Zr13Nb alloy// SURFACE & COATINGS TECHNOLOGY. -Vol. 258, (2014), s.1239-1248
Weryfikacja:
Politechnika Gdańska

wyświetlono 60 razy

Publikacje, które mogą cię zainteresować

Meta Tagi