Novel method for metal-oxide glass composite fabrication for use in thermoelectric devices

Abstrakt

A novel method for thermoelectric materials fabrication using a reduction of oxide precursors in hydrogen was reported. On the example of Bi-Sb, Bi-Sb-Te and Te-Ag-Ge-Sb compounds it was shown that this simple and easy method is suitable for fabrication of two-, three- and even multicomponent thermoelectric materials. It allows controlling a composition, microstructure and even type a of electrical charge carriers. As a result of reduction of oxide precursors a layered structure with an average thickness of layers equal tens of nanometers was formed. At the near-room temperature the best material with a figure of merit (ZT) close to 0.4 was Bi0.8Sb1.2Te3Ox reduced at 340 °C for 10 hours. At 350 °C a value of ZT=0.8 was reached by the (GeTe)0.85(AgSbTe2)0.15 (TAGS85) sample reduced twice at 400 °C for 10h.

Cytowania

  • 5

    CrossRef

  • 6

    Web of Science

  • 7

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
MATERIALS RESEARCH BULLETIN nr 76, strony 195 - 204,
ISSN: 0025-5408
Język:
angielski
Rok wydania:
2016
Opis bibliograficzny:
Bochentyn B., Karczewski J., Miruszewski T., Kusz B.: Novel method for metal-oxide glass composite fabrication for use in thermoelectric devices// MATERIALS RESEARCH BULLETIN. -Vol. 76, (2016), s.195-204
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.materresbull.2015.12.018
Weryfikacja:
Politechnika Gdańska

wyświetlono 27 razy

Publikacje, które mogą cię zainteresować

Meta Tagi