Mechanical behaviour was compared for glass/ polyester laminates manufactured in the boatbuilding plant using three methods: hand lay-up, vacuum bagging, infusion. Specimens were tested in dry condition and following accelerated water immersion test (70°C- corresponding to the exposure of 30 years at 19°C). In three point bending test 40-50% reduction in laminate strength was observed due to water immersion. The highest degradation was in samples manufactured using hand lay-up method, the differences in strength between both vacuum methods were insignificant. Interlaminar shear strength was reduced by 25% for infusion method which is recommended as the most efficient. Matrix plasticization and debondings as well as surface microcracks were responsible for reduction in strength for water conditioned specimens. However, no microstructural difference in type or intensity of internal damage was observed for the three sample types.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (3)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-011-0004-x
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Advances in Materials Science
nr 11,
strony 35 - 39,
ISSN: 1730-2439 - Język:
- angielski
- Rok wydania:
- 2011
- Opis bibliograficzny:
- Landowski M., Budzik M., Imielińska K.: On degradation of glass/polyester laminate immersed in water// Advances in Materials Science. -Vol. 11., nr. iss. 1 (2011), s.35-39
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2478/v10077-011-0004-x
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 72 razy
Publikacje, które mogą cię zainteresować
Experimental and Numerical Study on Mechanical Characteristics of Aluminum/Glass Fiber Composite Laminates
- M. E. Golmakani,
- T. Wiczenbach,
- M. Malikan
- + 3 autorów
Coupling of Blood Pressure and Subarachnoid Space Oscillations at Cardiac Frequency Evoked by Handgrip and Cold Tests: A Bispectral Analysis
- M. Gruszecki,
- Y. Tkachenko,
- J. Kot
- + 10 autorów