Processing of Ce0.8Gd0.2O2-δ barrier layers for solid oxide cells: The effect of preparation method and thickness on the interdiffusion and electrochemical performance

Abstrakt

Ce0.8Gd0.2O1.9 (CGO) barrier layers are required to mitigate the chemical reactions between Sr-containing oxygen electrode materials and Zr-based oxygen ion conductors in high-temperature solid oxide cells. Barrier layers produced by different methods were studied in this work. As a reference, a cell with no barrier layer was measured. The application of the powder-processed barrier layers, considerably increases the performance. For further comparison, thin and dense CGO layers were produced by a low-temperature spray pyrolysis process. Three different thicknesses were evaluated: ∼300 nm, ∼700 nm and ∼1500 nm. The best performance was found for the ∼700 nm thick CGO barrier layer. It showed low ohmic and polarisation resistances. The low thickness and high density of the CGO barrier layer were found to be the important factors. The cells with the ∼700 nm CGO barrier layers were also evaluated for their electrolysis performance as well as fuel cell durability.

Cytowania

  • 5

    CrossRef

  • 4

    Web of Science

  • 5

    Scopus

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY nr 40, strony 5626 - 5633,
ISSN: 0955-2219
Język:
angielski
Rok wydania:
2020
Opis bibliograficzny:
Molin S., Karczewski J., Kamecki B., Mroziński A., Wang S., Jasiński P.: Processing of Ce0.8Gd0.2O2-δ barrier layers for solid oxide cells: The effect of preparation method and thickness on the interdiffusion and electrochemical performance// JOURNAL OF THE EUROPEAN CERAMIC SOCIETY -Vol. 40,iss. 15 (2020), s.5626-5633
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jeurceramsoc.2020.06.006
Weryfikacja:
Politechnika Gdańska

wyświetlono 23 razy

Publikacje, które mogą cię zainteresować

Meta Tagi