Abstrakt

Stress corrosion cracking resistance of cold worked layers of 25 Cr duplex stainless steel grade UR52N+ has been investigated. The surface layers were performed through burnishing treatment. The residual stresses at surface layers were determined using grazing angle incidence X-ray diffraction method (g-sin2 Ψ). Corrosion tests were performed with the use of Slow Strain Rate Test technique in boiling 35% MgCl2 solution. It has been shown that burnishing treatment increases corrosion resistance of the steel. Stress corrosion cracking resistance depends on the magnitude of cold work at surface layers. High level of cold work decreases corrosion resistance.

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Opublikowano w:
Solid State Phenomena nr 165, strony 118 - 123,
ISSN: 1012-0394
Język:
angielski
Rok wydania:
2010
Opis bibliograficzny:
Łabanowski J., Ossowska A.: Properties of surface layers of duplex stainless steel after burnishing processes// Solid State Phenomena. -Vol. 165., (2010), s.118-123
Weryfikacja:
Politechnika Gdańska

wyświetlono 24 razy

Publikacje, które mogą cię zainteresować

Meta Tagi