Single crystals of SrCo2Al and BaCo2Al9 were grown using a self-flux method. A LeBail analysis of the powder X-ray diffraction patterns show that both compounds crystallize in a hexagonal (P6/mmm) crystal structure with lattice parameters: a = 7.8995(1) Å, c = 3.9159(1) Å for SrCo2Al9, and a = 7.9162(2) Å, c = 3.9702(1) Å for BaCo2Al9 aluminide. The low temperature analysis of the heat capacity measurements give a Sommerfeld coefficient γ = 4.99(6) mJ mol−1 K−2 for SrCo2Al9 and almost twice larger γ = 7.94(9) mJ mol−1 K−2 for BaCo2Al9. Resistivity measurements show metallic-like behavior, with reasonably large residual resistivity ratio RRR = 6 and 10 for SrCo2Al9 and BaCo2Al9, respectively. Neither heat capacity nor resistivity measurements reveal any phase transition down to 1.8 K.
Cytowania
-
6
CrossRef
-
0
Web of Science
-
6
Scopus
Autorzy (3)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF SOLID STATE CHEMISTRY
nr 289,
ISSN: 0022-4596 - Język:
- angielski
- Rok wydania:
- 2020
- Opis bibliograficzny:
- Ryżyńska Z., Klimczuk T., Winiarski M.: Single crystal growth and physical properties of MCo2Al9 (M= Sr, Ba)// JOURNAL OF SOLID STATE CHEMISTRY -Vol. 289, (2020), s.121509-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jssc.2020.121509
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 153 razy
Publikacje, które mogą cię zainteresować
Crystal structure and physical properties of new Ca2TGe3 (T = Pd and Pt) germanides
- T. Klimczuk,
- W. Xie,
- M. J. Winiarski
- + 4 autorów
Structure and paramagnetism in weakly correlated Y8Co5
- T. Klimczuk,
- V. A. .. Sidorov,
- A. Szajek
- + 6 autorów