Spray pyrolysis of doped-ceria barrier layers for solid oxide fuel cells

Dagmara Grudzień; Aleksander Chrzan; Jakub Karczewski; Sebastian Molin; Piotr Jasiński

doi:10.1016/j.surfcoat.2017.01.066

Spray pyrolysis of doped-ceria barrier layers for solid oxide fuel cells

Abstrakt

Gadolinium doped ceria (Ce0.8Gd0.2O2 − x-CGO) layer fabricated by spray pyrolysis is investigated as the diffusion barrier for solid oxide fuel cell. It is deposited between the La0.6Sr0.4FeO3 − δ cathode and the yttria stabilized zirconia electrolyte to mitigate harmful interdiffusion of elements. The parameters of the fabrication process are linked to the measured area specific resistances of the symmetrical cells and the efficiency of the fuel cells. Results show, that application of 800 nm thick barrier effectively hinder negative reactions, while 400 nm thick layer is sufficient to prevent degradation of the Ohmic resistance.

Cytowania

1 3

CrossRef
0

Web of Science
1 4

Scopus

Autorzy (5)

Dagmara Grudzień
Aleksander Chrzan
Jakub Karczewski dr hab. inż.
Sebastian Molin
- Technical University of Denmark, Department of Energy Conversion and Storage
Piotr Jasiński prof. dr hab. inż.

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

pełna treść artykułu zobacz w serwisie zewnętrznym otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:: Publikacja w czasopiśmie
Typ:: artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:: SURFACE & COATINGS TECHNOLOGY nr 313, strony 168 - 176,
ISSN: 0257-8972
Język:: angielski
Rok wydania:: 2017
Opis bibliograficzny:: Szymczewska D., Chrzan A., Karczewski J., Molin S., Jasiński P.: Spray pyrolysis of doped-ceria barrier layers for solid oxide fuel cells// SURFACE & COATINGS TECHNOLOGY. -Vol. 313, (2017), s.168-176
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.surfcoat.2017.01.066
Weryfikacja:: Politechnika Gdańska