Resistivity, dc magnetization, and heat capacity measurements are reported for superconducting NaBi. Tc, the electronic contribution to the specific heat γ, the ΔCp/γTc ratio, and the Debye temperature are found to be 2.15 K, 3.4 mJ mol−1 K−2, 0.78, and 140 K respectively. The calculated electron–phonon coupling constant (λep = 0.62) implies that NaBi is a moderately coupled superconductor. The upper critical field and coherence length are found to be 250 Oe and 115 nm, respectively. Electronic structure calculations show NaBi to be a good metal, in agreement with the experiments; the px and py orbitals of Bi dominate the electronic states at the Fermi Energy.
Cytowania
-
1 4
CrossRef
-
0
Web of Science
-
2 2
Scopus
Autorzy (8)
-
S. K. Kushwaha
- Princeton University Department of Chemistry
-
J. W. Krizan
- Princeton University Department of Chemistry
-
J. Xiong
- Princeton University Department of Physics
-
Q. D. Gibson
- Princeton University Department of Chemistry
-
T. Liang
- Princeton University Department of Physics
-
N.p. Ong
- Princeton University Department of Physics
-
R. J. Cava
- Princeton University Department of Chemistry,
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF PHYSICS-CONDENSED MATTER
nr 26,
wydanie 21,
strony 1 - 6,
ISSN: 0953-8984 - Język:
- angielski
- Rok wydania:
- 2014
- Opis bibliograficzny:
- Kushwaha S., Krizan J., Xiong J., Klimczuk T., Gibson Q., Liang T., Ong N., Cava R.: Superconducting properties and electronic structure of NaBi// JOURNAL OF PHYSICS-CONDENSED MATTER. -Vol. 26, iss. 21 (2014), s.1-6
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1088/0953-8984/26/21/212201
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 119 razy