Wyszukiwarka
Abstrakt
The niobium rich selenide compound Nb5Se4 was synthesized at ambient pressure by high-temperature solid–state reaction in a sealed Ta tube. Resistivity and heat capacity measurements reveal that this compound is superconducting, with a Tc = 1.85K. The electronic contribution to the specific heat γ and the Debye temperature are found to be 18.1 mJmol−1K−2 and 298 K respectively. The calculated electron-phonon coupling constant λep = 0.5 and the ΔCp/γTc = 1.42 ratio imply that Nb5Se4 is a weak coupling BCS superconductor. The upper critical field and coherence length are found to be 1.44 T and 15.1 nm, respectively.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
1
Scopus
Autorzy (5)
-
K. Baroudi
- Princeton University Department of Chemistry
-
J.w. Krizan
- Princeton University Department of Chemistry
-
R.j. Cava
- Princeton University Department of Chemistry
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF ALLOYS AND COMPOUNDS
nr 649,
strony 906 - 909,
ISSN: 0925-8388 - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Klimczuk T., Baroudi K., Krizan J., Kozub A., Cava R.: Superconductivity in the niobium-rich compound Nb5Se4// JOURNAL OF ALLOYS AND COMPOUNDS. -Vol. 649, (2015), s.906-909
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jallcom.2015.06.281
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 127 razy
Publikacje, które mogą cię zainteresować
Superconductivity in LiGa2Ir Heusler type compound with VEC = 16
- K. Górnicka,
- G. Kuderowicz,
- M. Winiarski
- + 2 autorów
2021
Structure redetermination, transport and thermal properties of the YNi3Al9 compound
- I. Oshchapovskyy,
- E. E. Oyeka,
- T. Tran
- + 2 autorów
2023