A series of porous, single phase Sr0.96Y0.04Ti1-xNbxO3 samples was obtained using a wet synthesis method (modified citrate sol-gel) method. Temperature-programmed reduction (TPR) and temperature-programmed oxidation (TPO) measurements have shown high stability of the obtained material in variable (oxidizing/reducing) atmospheres. All samples exhibit high conductivity in hydrogen atmosphere with the highest value (around 1S/cm) in case of the material with nominal composition Sr0.96Y0.04Ti0.98Nb0.02O3. Moreover, measurements of the electrical resistance carried out for Sr0.96Y0.04Ti1-xNbxO3 samples in oxidation-reduction cycles confirmed the high stability of these materials and extremely rapid electrical response with change of the atmosphere . The results of the studies show that highly porous niobium and yttrium-doped strontium titanate materials can be used as a component for SOFC anodes or resistance gas sensor.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
1
Scopus
Autorzy (2)
-
Ewa Drożdż
- Akademia Górniczo-Hutnicza Wydział Inżynierii Materiałowej i Ceramiki Katedra Chemii Nieorganicznej
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
SOLID STATE IONICS
nr 320,
strony 305 - 309,
ISSN: 0167-2738 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Drożdż E., Karczewski J.: Synthesis and properties of porous Sr 0.96 Y 0.04 Ti 1−x Nb x O 3// SOLID STATE IONICS. -Vol. 320, (2018), s.305-309
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ssi.2018.03.018
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 147 razy
Publikacje, które mogą cię zainteresować
Structural and electrical properties of Cr-doped SrTiO 3 porous materials
- A. Łącz,
- Ł. Łańcucki,
- R. Lach
- + 2 autorów